Processing–Property Relations in Grain‐Oriented Lead Metaniobate Ceramics Fabricated by Layered Manufacturing
Author(s) -
Hagh Nader Marandian,
aka Kazuhiro,
Allahverdi Mehdi,
Safari Ahmad
Publication year - 2005
Publication title -
journal of the american ceramic society
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.9
H-Index - 196
eISSN - 1551-2916
pISSN - 0002-7820
DOI - 10.1111/j.1551-2916.2005.00561.x
Subject(s) - materials science , equiaxed crystals , ceramic , composite material , crystallite , sintering , grain size , microstructure , mineralogy , metallurgy , chemistry
Highly grain‐oriented lead metaniobate (PbNb 2 O 6 ; PN) ceramics were prepared by a layered manufacturing (LM) process. This process has enabled us to obtain a net‐shaped piezoelectric ceramic component with grain orientation of f ∼89%, and improvement in electromechanical properties. The LM feedstock (filament) includes equiaxed (matrix; 90 vol%) and anisometric PN templates (10 vol%), both dispersed uniformly in a thermoplastic binder. The needle‐like PN templates were synthesized by molten salt synthesis technique, while the equiaxed PN powder was prepared by conventional ceramic processing methods. The processing conditions were studied and optimized to obtain orthorhombic phase fine powder and anisometric templates.Samples were obtained through layer‐by‐layer deposition of the filament through a small diameter (500 μm) nozzle. After binder removal, the PN samples were sintered in a temperature range of 1150°–1300°C for 1 h. SEM observation revealed strong grain orientation perpendicular to the deposition direction. Relative permittivity at the Curie point ( T c : 560°C) was 18 100 and 14 600 for the LM and random polycrystalline samples, respectively. Improved properties in piezoelectric figure of merit by 71%, d 33 by 23%, and g 33 by 31% were observed in the grain‐oriented samples. Remnant polarization also showed about 80% improvement, increasing from 4.5 to 8.1 μC/cm 2 for the grain‐oriented LM samples.