The Effect of Mechanical Cycling and Different Misfit Levels on Vicker's Microhardness of Retention Screws for Single Implant‐Supported Prostheses
Author(s) -
Assunção Wirley Gonçalves,
Jorge Juliana Ribeiro Pala,
Dos Santos Paulo Henrique,
Barão Valentim Adelino,
Gomes Érica Alves,
Delben Juliana Aparecida
Publication year - 2011
Publication title -
journal of prosthodontics
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.902
H-Index - 60
eISSN - 1532-849X
pISSN - 1059-941X
DOI - 10.1111/j.1532-849x.2011.00753.x
Subject(s) - indentation hardness , cycling , materials science , significant difference , implant , dentistry , orthodontics , composite material , medicine , surgery , microstructure , archaeology , history
Purpose: The aim of this study was to evaluate the effect of mechanical cycling and different misfit levels on Vicker's microhardness of retention screws for single implant‐supported prostheses. Materials and Methods: Premachined UCLA abutments were cast with cobalt‐chromium alloy to obtain 48 crowns divided into four groups (n = 12). The crowns presented no misfit in group A (control group) and unilateral misfits of 50 μm, 100 μm, and 200 μm in groups B, C, and D, respectively. The crowns were screwed to external hexagon implants with titanium retention screws (torque of 30 N/cm), and the sets were submitted to three different periods of mechanical cycling: 2×10 4 , 5×10 4 , and 1×10 6 cycles. Screw microhardness values were measured before and after each cycling period. Data were evaluated by two‐way ANOVA and Tukey's test ( p < 0.05). Results: Mechanical cycling statistically reduced microhardness values of retention screws regardless of cycling periods and groups. In groups A, B, and C, initial microhardness values were statistically different from final microhardness values ( p < 0.05). There was no statistically significant difference for initial screw microhardness values ( p > 0.05) among the groups; however, when the groups were compared after mechanical cycling, a statistically significant difference was observed between groups B and D ( p < 0.05). Conclusions: Mechanical cycling reduced the Vicker's microhardness values of the retention screws of all groups. The crowns with the highest misfit level presented the highest Vicker's microhardness values.