Effects of 6 Months of Aging in Water on Hardness and Surface Roughness of Two Microhybrid Dental Composites
Author(s) -
De Moraes Rafael Ratto,
Marimon José Laurindo Machado,
Jochims Schneider Luis Felipe,
Sinhoreti Mário Alexandre Coelho,
CorrerSobrinho Lourenço,
Bueno Márcia
Publication year - 2008
Publication title -
journal of prosthodontics
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.902
H-Index - 60
eISSN - 1532-849X
pISSN - 1059-941X
DOI - 10.1111/j.1532-849x.2007.00295.x
Subject(s) - distilled water , knoop hardness test , materials science , surface roughness , charisma , composite material , surface finish , hardness , indentation hardness , microstructure , chemistry , theology , philosophy , chromatography
Purpose: This study assessed the effect of 6 months of aging in water on surface roughness and surface/subsurface hardness of two microhybrid resin composites. Materials and Methods: Filtek Z250 and Charisma were tested. Cylindrical specimens were obtained and stored in distilled water for 24 hours or 6 months, at 37°C. For Knoop hardness evaluation, the specimens were transversely wet‐flattened, and indentations were made on surface and subsurface layers. Data were submitted to three‐way ANOVA and Tukey's test (α≤ 0.05). Surface roughness baseline measurements were made at 24 hours and repeated after 6 months of storage. Data were submitted to repeated measures ANOVA and Tukey's test (α≤ 0.05). Results: Surface hardness (KHN, kg/mm 2 ) means (± standard deviation) ranged from 55 ± 1 to 49 ± 4 for Z250 and from 50 ± 2 to 41 ± 3 for Charisma, at 24 hours and 6 months, respectively. Subsurface means ranged from 58 ± 2 to 61 ± 3 for Z250 and from 50 ± 1 to 54 ± 2 for Charisma, at 24 hours and 6 months. For both composites, the aged specimens presented significantly softer surfaces ( p < 0.01). For the subsurface hardness, alteration after storage was detected only for Charisma, which presented a significant rise in hardness ( p < 0.01). Z250 presented significantly harder surface and subsurface layers in comparison with Charisma. Surface roughness (Ra, μm) means ranged from 0.07 ± 0.00 to 0.07 ± 0.01 for Z250 and from 0.06 ± 0.01 to 0.07 ± 0.01 for Charisma, at 24 hours and 6 months, respectively. For both composites, no significant roughness alteration was detected during the study ( p = 0.386). Conclusions: The 6‐month period of storage in water presented a significant softening effect on the surfaces of the composites, although no significant deleterious alteration was detected for the subsurface hardness. In addition, the storage period had no significant effect on the surface roughness of the materials.