FRACTURE CHARACTERISTICS OF BOROSILICATE GLASSES REINFORCED BY METALLIC PARTICLES
Author(s) -
Dlouhy I.,
Reinisch M.,
Boccaccini A. R.,
Knott J. F.
Publication year - 1997
Publication title -
fatigue and fracture of engineering materials and structures
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.887
H-Index - 84
eISSN - 1460-2695
pISSN - 8756-758X
DOI - 10.1111/j.1460-2695.1997.tb01484.x
Subject(s) - materials science , borosilicate glass , fracture toughness , composite material , volume fraction , toughness , molybdenum , particle (ecology) , plasticity , fracture (geology) , metallurgy , oceanography , geology
— The fracture behaviour of borosilicate glass reinforced by molybdenum and/or vanadium particles has been investigated. For the addition of 5 vol% molybdenum particles, two processing procedures have been tested and the influence of volume fraction of vanadium particles (in the range 2 to 30 vol%) on fracture resistance has been assessed. The use of chevron‐notched specimens in three‐point bending has been shown to be a reliable method for the evaluation of fracture toughness even at toughness levels of order 0.7 to 1.3 MPa √m. The existence of subtle differences in fracture behaviour of glass‐composites having comparable volume fractions of molybdenum particles but obtained by two different processing procedures has been established by statistical treatment of the fracture toughness data. An increase in the volume fraction of metallic particles results in an increase of the fracture resistance and the measured fracture toughness level. Toughening mechanisms which have been identified include both the plastic deformation of particles and the bridging of cracks by ductile particles. Some particle cleavage and debonding has been observed, which indicates that a decrease in particle plasticity, probably induced by processing or due to constraints imposed by the rigid matrix, is responsible for a smaller than expected enhancement of the fracture toughness.