STATISTICAL INVESTIGATION OF THE BEHAVIOUR OF SMALL CRACKS AND FATIGUE LIFE IN CARBON STEELS WITH DIFFERENT FERRITE GRAIN SIZES
Author(s) -
Goto M.
Publication year - 1994
Publication title -
fatigue and fracture of engineering materials and structures
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.887
H-Index - 84
eISSN - 1460-2695
pISSN - 8756-758X
DOI - 10.1111/j.1460-2695.1994.tb00262.x
Subject(s) - materials science , weibull distribution , ferrite (magnet) , carbon steel , composite material , grain size , metallurgy , mathematics , corrosion , statistics
— In order to study the relation between the scatter characteristics of small crack growth behaviour and fatigue life, rotatory bending fatigue tests of smooth specimens were carried out using 0.21% carbon steels of different ferrite grain sizes. Fifteen to eighteen specimens were fatigued at each stress amplitude, and the initiation and propagation behaviour of the cracks which led to the final fractures were examined for all the specimens. The physical basis of scatter in fatigue life was investigated, based on the successive observation of fatigue damage on the surface using the plastic replica technique, followed by an analysis of the data assuming a Weibull distribution. A statistical investigation of the physical basis of scatter in relation to the ferrite grain size was performed, i.e. the distributions for crack initiation life, crack propagation life, fatigue life and growth rate of small cracks. Finally, the fluctuation of crack growth rate was studied in relation to the application of a crack growth law for microstructurally small cracks.