APPLICATION OF LOCAL DAMAGE MODELS TO THE NUMERICAL ANALYSIS OF DUCTILE RUPTURE
Author(s) -
Sun D.Z.,
Siegele D.,
Voss B.,
Schmitt W.
Publication year - 1989
Publication title -
fatigue and fracture of engineering materials and structures
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.887
H-Index - 84
eISSN - 1460-2695
pISSN - 8756-758X
DOI - 10.1111/j.1460-2695.1989.tb00527.x
Subject(s) - void (composites) , coalescence (physics) , constitutive equation , materials science , finite element method , von mises yield criterion , structural engineering , nucleation , mechanics , composite material , engineering , physics , thermodynamics , astrobiology
— Two damage models were implemented into the finite element program ADINA to study the correlation between microscopical damage and macroscopical material failure. In the first model, based on the Gurson yield function the nucleation, growth and the coalescence of voids were incorporated into the constitutive relations. In the second model the void growth was determined according to the Rice and Tracey model using the von Mises yield function, and material failure was simulated by eliminating the elements where the critical void growth ratio was exceeded. The numerical results for the local and global behaviour of the specimens were compared with experiments. The generality of the damage parameters was checked by investigating several specimen geometries. Both damage models deliver qualitatively consistent results with regard to the influence of the stress triaxiality on the void growth and on the beginning of the material failure. However, the Gurson model gives a more accurate numerical simulation because the damage development and the stress drop continue after the onset of void coalescence while the critical void growth model causes less convergence problems in the simulation of large crack extension. The J n ‐curve was estimated on the basis of both models.