FATIGUE CRACK INITIATION IN ALUMINIUM ALLOYS UNDER PROGRAMMED BLOCK LOADING
Author(s) -
Gabra M.,
Bathias C.
Publication year - 1984
Publication title -
fatigue and fracture of engineering materials and structures
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.887
H-Index - 84
eISSN - 1460-2695
pISSN - 8756-758X
DOI - 10.1111/j.1460-2695.1984.tb00356.x
Subject(s) - materials science , aluminium , bending , fatigue testing , crack closure , structural engineering , three point flexural test , composite material , metallurgy , fracture mechanics , engineering
— Tests for fatigue crack initiation were carried out on two different aluminium alloys. Results and analysis of initiation under constant amplitude loading are presented; elastic and elastoplastic analyses are applied. Initiation under programmed block loading is investigated and damage accumulation is discussed. Tests were performed on two notch root radii:5 and 0.5mm. The electric potential method was used to detect fatigue crack initiation. Three point bending tests on smooth specimens were carried out to follow the evolution of damage during the crack initiation phase.