Reaction Synthesis of Aluminum Nitride–Boron Nitride Composites Based on the Nitridation of Aluminum Boride
Author(s) -
Zhang GuoJun,
Yang JianFeng,
Ando Motohide,
Ohji Tatsuki
Publication year - 2002
Publication title -
journal of the american ceramic society
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.9
H-Index - 196
eISSN - 1551-2916
pISSN - 0002-7820
DOI - 10.1111/j.1151-2916.2002.tb00559.x
Subject(s) - materials science , boride , sintering , nitride , boron nitride , aluminium , differential thermal analysis , composite material , thermogravimetry , microstructure , metallurgy , layer (electronics) , chemical engineering , diffraction , physics , optics , engineering
Aluminum nitride–boron nitride (AlN–BN) composites were prepared based on the nitridation of aluminum boride (AlB 2 ). AlN powder was added to change the BN volume fraction in the obtained composites. Thermogravimetry–differential thermal analysis (TG‐DTA), X‐ray diffractometry, and the nitridation ratio were used to investigate the nitridation process of AlB 2 . At ∼1000°C, a sharp exothermic peak occurred in the DTA curve, corresponding to the rapid nitridation of aluminum in AlB 2 . On the other hand, the nitridation of the transient phase, Al 1.67 B 22 , was very slow when the temperature was <1400°C. However, the nitridation speed obviously accelerated at temperatures >1600°C. The pressure of the nitrogen atmosphere was also an important factor; high nitrogen pressure remarkably promoted nitridation. Treatment at 2000°C was disadvantageous for nitridation, because of the rapid formation of a dense surface layer that inhibited nitrogen diffusion into the specimen interior. Three specimens, with 5 wt% Y 2 O 3 additive and different BN contents, were prepared by pressureless reactive sintering, according to the determined sintering schedule. Electron microscopy (scanning and transmission) observations revealed that the in‐situ ‐formed BN flakes were homogeneously and isotropically distributed in the AlN matrix. A schematic mechanism for microstructural formation was developed, based on the results of nitridation and the microstructural features of the obtained composites. The obtained composites, with a low BN content, exhibited a high bending strength, comparable to that of reported hot‐pressed AlN–BN composites.