Fabrication of Porous Ceramics with Unidirectionally Aligned Continuous Pores
Author(s) -
Zhang GuoJun,
Yang JianFeng,
Ohji Tatsuki
Publication year - 2001
Publication title -
journal of the american ceramic society
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.9
H-Index - 196
eISSN - 1551-2916
pISSN - 0002-7820
DOI - 10.1111/j.1151-2916.2001.tb00849.x
Subject(s) - slurry , porosity , materials science , fabrication , ceramic , composite material , coating , medicine , alternative medicine , pathology
Porous alumina ceramics with unidirectionally aligned continuous pores were fabricated via the slurry coating of fugitive fiber. Cotton thread was coated with ceramic slurry by pulling it through the slurry, and specimens were produced by spooling the coated thread. The obtained porous alumina ceramics had an average pore diameter of 165 μm, 35% open porosity, and a bending strength of 160 MPa. It was suggested that the pore size and the porosity could be adjusted using the diameter of the cotton thread and the solids concentration of the slurry, respectively.