Modeling the Ultimate Tensile Strength of Unidirectional Glass‐Matrix Composites
Author(s) -
Dutton R. E.,
Pagano N. J.,
Kim R. Y.,
Parthasarathy T. A.
Publication year - 2000
Publication title -
journal of the american ceramic society
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.9
H-Index - 196
eISSN - 1551-2916
pISSN - 0002-7820
DOI - 10.1111/j.1151-2916.2000.tb01166.x
Subject(s) - ultimate tensile strength , composite material , materials science , matrix (chemical analysis) , glass fiber
The ultimate tensile strengths of a unidirectional glass‐matrix composite were measured as a function of fiber volume fraction. The results were compared with predictions, using a refined solution of the stress field generated by an axisymmetric damage model, which incorporated the effect of stress concentration in the fiber caused by the presence of a matrix crack both before and after deflection at the fiber/matrix interface. Two possible locations for the fiber failure were considered: (1) at a transverse matrix crack, near a bonded fiber/coating interface and (2) at the tip of a debond, at the fiber/coating interface. At low fiber volume fractions, the measured ultimate tensile strength matched the prediction calculated, assuming no crack deflection. For higher volume fractions, the predictions calculated for a debonded crack matched the observed values. The model results were relatively insensitive to debond length and interfacial shear stress for the range of values in this study. In comparison, the global load‐sharing model, which does not account for the stress singularity at the fiber/matrix interface, was found to overpredict the values of the ultimate tensile strength for all fiber volume fractions. An important contribution of the present work was to introduce the use of fiber volume fraction as a parameter for testing theoretical predictions of the mode of fiber failure.