Sintering of Platelike Iron(III) Oxide Powders
Author(s) -
Yamaguchi Takashi,
Mian Guo
Publication year - 1991
Publication title -
journal of the american ceramic society
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.9
H-Index - 196
eISSN - 1551-2916
pISSN - 0002-7820
DOI - 10.1111/j.1151-2916.1991.tb07814.x
Subject(s) - platy , acicular , sintering , hematite , materials science , oxide , metallurgy , chemical engineering , iron oxide , mineralogy , composite material , chemistry , microstructure , engineering
Packing and sintering of platelike hematite powders were studied with a special emphasis on pore behavior, and the results were compared with those for acicular powders. Platy particles gave a relatively high green density of 65% of the theoretical value, but did not achieve high fired densities. This is in strong contrast to acicular powders, in which high fired densities were reached from a relatively low green density under the same firing conditions. Features observed with platy particles have been interpreted as being due to the wedgelike pores which tend to close at the early stages of densification.