Dissolution Rates of Silicate Glasses in Water at pH 7
Author(s) -
Perera Gunarathna,
Doremus Robert H.,
Lanford William
Publication year - 1991
Publication title -
journal of the american ceramic society
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.9
H-Index - 196
eISSN - 1551-2916
pISSN - 0002-7820
DOI - 10.1111/j.1151-2916.1991.tb04096.x
Subject(s) - borosilicate glass , dissolution , aluminosilicate , silicate , soda lime glass , soda lime , mineralogy , materials science , dissolved silica , quartz , silicate glass , chemical engineering , metallurgy , chemistry , composite material , biochemistry , engineering , catalysis
Dissolution rates of different glasses in buffered solutions of constant pH of 7 were measured by weight change, profilometry, and ion implantation with Rutherford backscattering. Rates with different techniques agreed within experimental error. Natural obsidian glass dissolved most slowly, at a rate comparable with those of quartz and crystalline aluminosilicate minerals. Commercial soda–lime glass containing alumina dissolved slowly, at about the same rate as vitreous silica; soda–lime silicate glasses both commercial and laboratory without alumina dissolved much more rapidly. Pyrex borosilicate glass dissolved at a rate intermediate between those of soda–lime silicate glasses with and without alumina; at room temperature Pyrex borosilicate glass dissolved about 100 times faster than a commercial soda–lime glass containing alumina. We suggest that surface structure is the main factor determining the relative dissolution rates of silicate glasses. Glasses with transformed surface layers caused by hydration dissolve most rapidly; phase separation and openness of the glass structure are also important factors.