Retrogradation of partially gelatinised potato starch prepared by ball milling
Author(s) -
Fu Zongqiang,
Wu Min,
Zhang Hai,
Wang Jiahui
Publication year - 2018
Publication title -
international journal of food science and technology
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.831
H-Index - 96
eISSN - 1365-2621
pISSN - 0950-5423
DOI - 10.1111/ijfs.13683
Subject(s) - starch , retrogradation (starch) , food science , chemistry , degree (music) , potato starch , ball mill , materials science , amylose , composite material , physics , acoustics
Summary This study was performed to evaluate the effect of partial gelatinisation on the retrogradation of modified potato starch. The partially gelatinised starches with gelatinisation degree at mean levels of 22.47%, 49.18%, 76.80% and 86.19% were prepared by ball milling (0.5, 1.5, 3 and 10 h). The thermal properties and crystal structure of retrograded starch were examined during 21 days of refrigerated storage at 4 °C. Retrograded starch with high initial gelatinisation degree (86.19%) showed higher retrogradation enthalpy of 6.12 ± 0.18 J g −1 and lower onset temperature of 45.41 ± 0.24 °C than sample with low gelatinisation degree (22.47%) where the results were 1.32 ± 0.18 J g −1 and 54.05 ± 0.03 °C, respectively. During storage, two peaks in the X‐ray diffractograms for starch with high gelatinisation degree appeared and increased rapidly, while the peaks for starch with low gelatinisation degree increased slowly. These results suggest that a certain amount of remainder crystals presented in partially gelatinised starch impeded the retrogradation.