Combined effects of SiO 2 ratio and purity on physical properties and microstructure of in situ alumina‐mullite ceramic
Author(s) -
Salomão Rafael,
Fernandes Leandro,
Spera Natalia C. M.
Publication year - 2021
Publication title -
international journal of applied ceramic technology
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.4
H-Index - 57
eISSN - 1744-7402
pISSN - 1546-542X
DOI - 10.1111/ijac.13733
Subject(s) - mullite , materials science , microstructure , flexural strength , impurity , sintering , porosity , silica fume , calcination , composite material , ceramic , grain size , amorphous solid , mineralogy , compressive strength , crystallography , chemistry , biochemistry , organic chemistry , catalysis
The in situ formation of mullite (Al 6 Si 4 O 13 ) is a complex process based on solid‐state reactions strongly affected by the characteristics of Al 2 O 3 and SiO 2 sources. This study investigated the combined effects of variable SiO 2 /Al 2 O 3 ratios and the presence of low‐melting‐point impurities on the physical properties and microstructure of in situ alumina‐mullite ceramics. Two grades of synthetic amorphous silica, known as microsilica, of similar physical properties and significant differences in the content of alkali‐based impurities (0.8 and 3.6 wt%), were combined with thin calcined alumina particles in different proportions (from silica‐free up to stoichiometric mullite), pressed and sintered. The samples were tested for total porosity, flexural strength, and pore size distribution, and their crystalline phases and microstructures formed were investigated. Small amounts of both microsilica grades (up to 8.9 wt%) hindered the densification of the alumina‐mullite matrix and favored grain growth events, increasing porosity and reducing strength. For samples containing higher microsilica loads (16.4–28.2 wt%), the impurities content significantly affected the amount of liquid phases formed. Such impurities altered the ratio and shape of the pores and the total amount of mullite after sintering. Therefore, different microstructures and levels of flexural strength and total porosity were observed.