Microwave hybrid fast sintering of red clay ceramics
Author(s) -
Pitolli Lyra Gabriela,
Santos Valdemir,
Maria de Jesus Agnolon Pallone Eliria,
Herta Goldschmidt Aliaga Kiminami Ruth,
Carlos De Santis Bruno,
Adriano Rossignolo João
Publication year - 2021
Publication title -
international journal of applied ceramic technology
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.4
H-Index - 57
eISSN - 1744-7402
pISSN - 1546-542X
DOI - 10.1111/ijac.13676
Subject(s) - materials science , sintering , ceramic , microstructure , scanning electron microscope , porosity , thermogravimetric analysis , composite material , metallurgy , chemical engineering , engineering
This work aimed to examine the performance of the hybrid sintering of clay ceramic in a microwave furnace, compared to the sintering process in a conventional furnace. The raw materials were subjected to X‐ray fluorescence, loss on ignition (LOI), X‐ray diffraction, particle size distribution, real specific mass, and thermogravimetric analyses. The red clay ceramic mass was prepared, extruded, pre‐sintered in a conventional furnace at 600°C/60 min, and sintered at temperatures between 700 °C and 1100 °C. The sintering conventional (resistive oven) was carried out for 60 min with a heating rate of 10°C/min. In the microwave furnace, the sintering times were 5, 10, and 15 min, with a heating rate of 50°C/min, with a sintering chamber coated with silicon carbide (susceptor). The sintered specimens were characterized according to linear shrinkage, water absorption, apparent porosity, apparent specific mass, X‐ray diffraction, Raman spectroscopy analysis, spectroscopy analysis in the ultraviolet and visible regions, microhardness, and scanning electron microscopy. The results showed that microwave sintering promoted an increase in the microhardness and apparent specific mass, and reduction in water absorption and apparent porosity values, due to greater densification in the microstructure. The best results occurred for specimens sintered at 1100°C.