Open AccessEvolution of microstructure, texture and residual stress of AZ31 Mg alloy in hot extrusion process
Author(s) -
Lei Kang,
Weirong Liu,
Xiongbo Zhang,
Leng Chen
Publication year - 2021
Publication title -
materials research express
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.383
H-Index - 35
ISSN - 2053-1591
DOI - 10.1088/2053-1591/ac0736
Subject(s) - extrusion , microstructure , residual stress , materials science , metallurgy , texture (cosmology) , alloy , process (computing) , computer science , artificial intelligence , image (mathematics) , operating system
In this work, we have investigated the microstructure, texture, and residual stress of AZ31 Mg alloy at several higher extrusion temperatures (360 °C, 380 °C, 400 °C) and speeds (1 m min −1 , 2 m min −1 , 3 m min −1 ). Results show that the bimodal microstructure can be observed in all extruded Mg alloys, consisting of the fine grains in dynamic recrystallization (DRX) zone and the coarse grains in non-dynamic recrystallization (non-DRX) zone. The non-monotonic relation between average grain diameter and extrusion speed has been found. It is attributed to the promoted nucleation and inhibited grain growth at higher extrusion speed. The bimodal microstructure can maintain the stability of sharp {0002} basal texture. Schmid Factor (SF) is calculated to explain the mechanism of basal texture formation. By employing XRD with cos α method, the residual stress has been measured. The major origin of residual stress release at higher extrusion temperature is the grain growth, rather than the strengthening of basal texture. The anisotropy of residual stress distribution is related to the coupling effect of grain growth and evolution of basal texture of extruded Mg alloys.