Open AccessErosion studies of plasma sprayed WC-12%Co, Cr3C2-25%NiCr, 80%Ni-20%Cr, 87%Al2O3-13%TiO2 coatings on ASTM A36 steel
Author(s) -
Varun Panwar,
Neel Kanth Grover,
Vikas Chawla
Publication year - 2020
Publication title -
materials research express
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.383
H-Index - 35
ISSN - 2053-1591
DOI - 10.1088/2053-1591/ab7072
Subject(s) - nichrome , materials science , erosion , substrate (aquarium) , metallurgy , coating , thermal spraying , composite material , biology , paleontology , oceanography , geology
WC-12%Co, Cr 3 C 2 -25%NiCr, 80%Ni-20%Cr, 87%Al 2 O 3 -13%TiO 2 coatings were deposited by Air Plasma Spray (APS) technique on ASTM A36 steel. Erosion behaviour of sprayed coated samples were investigated at three different impact angles (45°, 60° and 90°). The mechanism of erosion was investigated on uncoated and coated samples. The rate of erosion of the substrate first increased with increasing angle of impact and then gradually decreased. But the erosion rate of the coated samples increased steadily. Substrate shows the higher metal removal whereas coating shows the higher erosion resistance. WC-12%Co coated samples performed well in erosion testing and offered best erosion resistance as compared to the substrate and all other coatings. Ductile fracture takes place on substrate material at higher impact angle. Overall, all the coated samples have shown less erosion propensity when compare to the bare one.