Optical properties of sol-gel coatings containing silver nanoparticles
Author(s) -
С Н Степин,
T A Xolmurodov,
O O Mirzaev,
В Е Катнов
Publication year - 2020
Publication title -
iop conference series. materials science and engineering
Language(s) - English
Resource type - Journals
eISSN - 1757-899X
pISSN - 1757-8981
DOI - 10.1088/1757-899x/911/1/012007
Subject(s) - materials science , anti reflective coating , coating , silicon dioxide , chemical engineering , nanometre , silver nanoparticle , nanoparticle , auger electron spectroscopy , silicon , composite material , nanotechnology , metallurgy , physics , nuclear physics , engineering
The technology of receiving the antireflective coating increasing efficiency of use of sunlight in various service conditions is described. Suspensions of nanodimensional silicon dioxide with tetraethoxysilane as a precursor were synthesized to solve the assigned task. The received suspensions were applied by a dipping method on glass samples followed by the coating formation on a surface of the substrates at various temperatures. As a result of a cure of the received samples under natural conditions transparent film of about 500 nanometers thick having very low strength properties on the surface of glass were formed. Heat treatment led to the improvement of strength of coatings in process with increase of temperature up to 600 °C. Exceeding of this temperature resulted in cracking of coatings. In the course of heat treatment higher than 300 °C formation of a coating was accompanied by the thermolysis of silver nitrate that was introduced into silicon dioxide suspension with a formation of silver particles which size was in the nanoscale distance limits according to the results of Auger electron spectroscopy. Presence of evenly distributed silver nanoparticles provided an antireflective effect to coatings which at visual observation found expression in the form of the interference phenomenon. The obtained data confirmed prospects of use of nanosilver as a component of coatings on the basis of silicon dioxide in order to confer the antireflective properties.