Open AccessStudy on Mechanical Behaviors and Electrolyte Uptake of PVDF/PES/TiO2 Composite Fiber Separators
Author(s) -
Kai-Wen Cheng,
Xin Chen,
Shuai Liu,
Qingyuan Cao,
Weiwei Yu,
Weiwei Cui
Publication year - 2020
Publication title -
iop conference series. materials science and engineering
Language(s) - English
Resource type - Journals
eISSN - 1757-899X
pISSN - 1757-8981
DOI - 10.1088/1757-899x/768/2/022052
Subject(s) - materials science , ultimate tensile strength , differential scanning calorimetry , polyvinylidene fluoride , membrane , scanning electron microscope , crystallinity , electrolyte , toughness , electrospinning , composite material , composite number , fiber , tensile testing , chemical engineering , spinning , polymer , chemistry , electrode , biochemistry , physics , engineering , thermodynamics
In this paper, polyvinylidene fluoride (PVDF)/polyether sulfone (PES) spinning solution with different TiO 2 content was obtained by in-situ generation. The prepared spinning liquid was fabricated into PVDF/PES/TiO 2 composite membranes via electrospinning. The scanning electron microscopy (SEM), differential scanning calorimetry (DSC), mechanical properties, electrolyte uptake were conducted to test the performance of the obtained separators. The effect of TiO 2 contents on the properties of PVDF/PES separators was discussed. The experimental results show that the doping of nano-TiO 2 particles will enhance the performance of the separators. DSC test and electrolyte uptakes showed that the enthalpy of the polymer decreased and the electrolyte uptake increased with TiO 2 contents. When the separators contents 2 wt% TiO 2 , the enthalpy changes reach the maximum (28.259 J/g), and the crystallinity is measured to 26.99%. With the TiO 2 addition increases, the tensile strength of the membrane also showed the tendency of increasing first and then decreasing. At 6 wt%TiO 2 , the tensile strength of the membrane was better, reaching 5.606 N/mm 2 , and the toughness was the best. It shows that the addition of TiO 2 helps to enhance its tensile strength as well as toughness When the TiO 2 content is 6 wt%, the overall performance of the membrane is the best.