Open AccessWear behaviour of cast aluminium silicon (Al-Si) alloy in Dot 4 brake fluid
Author(s) -
Olawale Olarewaju Ajibola,
Sunday Aribo,
Oladeji Oluremi Ige,
Ojo Jeremiah Akinribide,
Samuel Olukayode Akinwamide,
Peter Apata Olubambi
Publication year - 2019
Publication title -
iop conference series. materials science and engineering
Language(s) - English
Resource type - Journals
eISSN - 1757-899X
pISSN - 1757-8981
DOI - 10.1088/1757-899x/628/1/012012
Subject(s) - aluminium , silicon , materials science , alloy , brake , metallurgy , composite material
The frictional sliding behaviour of cast Al-Si alloy was investigated with and without DOT 4 hydraulic brake fluid lubrication/environments. Cast Al-Si specimen was produced from wrought alloy and the specimen surface was metallurgically prepared. The as-cast product was characterized with aid of micro-hardness tester, the chemical composition was analysed by X-ray fluorescence (XRF), while X-ray diffraction (XRD) was used to identify phases present, microstructures and surface examinations were done on a high resolution metallurgical Optical Microscope. The properties of the polished and worn sample surfaces were examined by Scanning electron microscope (SEM) equipped with Energy dispersive X-ray (EDS) facilities. A 6mm diameter alumina ball under varying normal loads (3-10 N) was rubbed against the surface of the cast Al-Si coupon specimen. The dry and wet sliding wear behaviour was assessed based on the CoF-sliding time behaviour. From the results, the average CoF values of 0.9064 for dry and 0.2038 for wet contacts were obtained. Comparatively, 1.03E-06 and 4.21E-07 minimum wear intensities; and 467290 and 132170 wear resistances were obtained for dry and wet contacts respectively. Behaviour of cast Al-Si in DOT4 were compared with its performance in DOT3 regarding the hydraulic brake system application.