Open AccessStudy on the Behavior of Rigid Pavement Using Quarry Dust as a Partial Replacement of Sand and Sulfonated Naphthalene Formaldehyde (SNF) as an Admixture
Author(s) -
Khundrakpam Binod Singh,
Avani Chopra
Publication year - 2021
Publication title -
iop conference series. earth and environmental science
Language(s) - English
Resource type - Journals
eISSN - 1755-1307
pISSN - 1755-1315
DOI - 10.1088/1755-1315/889/1/012067
Subject(s) - crusher , curing (chemistry) , aggregate (composite) , cement , environmental science , geotechnical engineering , materials science , waste management , composite material , metallurgy , geology , engineering
Quarry dust is considered as a possible source of natural sand or fine aggregate in concrete construction work. This could reduce the problem of dumping of quarry dust as a byproduct from stone crusher factory. The experimental work investigates the optimum quarry dust percentage which can be adopted as replacement of fine aggregate in concrete mainly for rigid pavement. The quarry dust is added at different percentages of 0%, 20%, 40%, 60%, 80%, and 100% replacement of fine aggregate for M35 grade concrete thereby to find out the optimum content of quarry dust that can give better strength in concrete. Mix design has been developed for M35 grade of concrete as per IRC 044 – 2017(Mix Design for Concrete Pavement) and mix design ratio is found as 1: 1.6: 2.62 by using Sulfonated naphthalene formaldehyde (SNF) as an admixture at 1%, and 2%. The required water cement ratio was obtained as 0.39 according to table no.9 of IRC 044 for the target strength of 42.5 N/mm 2 . Optimum strength and workability test values of concrete made up for various proportions of quarry dust along with SNF are compared with conventional concrete of natural fine aggregate after 7 days and 28 days curing. It is found that the strength increased with the increase in curing time and the maximum strength at 28 days curing and 60% quarry dust replacement with 2% addition of SNF. The maximum strength of quarry replaced concrete is obtained as 40.3MPa, 5.6MPa, and 5.1MPa for compressive, flexural, and split tensile respectively.