Open AccessStructural analysis of TiO2and TiO2-Ag thin films and their antibacterial behaviors
Author(s) -
J.H. Hsieh,
Ri Yu,
Yu-Kaung Chang,
C Li
Publication year - 2012
Publication title -
journal of physics. conference series
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.21
H-Index - 85
eISSN - 1742-6596
pISSN - 1742-6588
DOI - 10.1088/1742-6596/339/1/012012
Subject(s) - materials science , anatase , rutile , amorphous solid , thin film , annealing (glass) , photocatalysis , doping , analytical chemistry (journal) , titanium oxide , sputtering , chemical engineering , absorption edge , nanotechnology , band gap , optoelectronics , crystallography , chemistry , composite material , biochemistry , chromatography , engineering , catalysis
TiO 2 (rutile and anatase) thin films was first prepared using reactive sputtering, in an Ar+O 2 plasma. In the 2nd stage of the experiment, various amounts (3, 7, and 10 at. %) of Ag was doped into the rutile film in order to form TiO 2 -Ag thin films. These films were annealed for one hour in Ar atmosphere, at 300, 400, and 500 °C. The films' structures were then examined using X-ray diffractometry. FESEM (field-emission scaning electron microscopy) was used to investigate the surface emergence of Ag particles. As for the examination of optical band gaps and absorption of these films, UV-Vis-NIR photometer was used. The results show that, in as-deposited condition, the addition of Ag might disrupt the growth of crystalline structure and cause the formation of amorphous films. After annealing, it is found that the structure tends to become anatase phase which is a metastable phase between amorphous titanium oxide and rutile. More importantly, the absorption of the Ag-doped films would be enhanced in the visible-light range. Some of the enhancement is clearly due to plasmon resonance effect. The Ag-doped samples have shown some antibacterial effect in dark. When irradiated with light, the samples show a synergistic behavior combining the bactericidal effect of Ag ions and photocatalytic effect of TiO 2 .