Open AccessThe Effect of Boron Addition on the corrosion behavior of Ni Cr Modental alloy prepared by powder metallurgy.
Author(s) -
Ali Hubi Haleem,
Haydar H. J. Jamal Al-Deen,
Ban Ahmed Shanan
Publication year - 2021
Publication title -
journal of physics. conference series
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.21
H-Index - 85
eISSN - 1742-6596
pISSN - 1742-6588
DOI - 10.1088/1742-6596/1973/1/012152
Subject(s) - metallurgy , materials science , corrosion , alloy , microstructure , powder metallurgy , tafel equation , inert gas , sintering , brinell scale , boron , electrochemistry , composite material , electrode , chemistry , organic chemistry
The powder metallurgy (PM) method was used to create the alloy. The sintering process was carried out in an inert high-temperature tube furnace in the presence of inert gas at a temperature of 1000 ° C for 8 hours (Argon). In this article, the effect of (B) at three wt.% (0.4,0.8,1.2) on the corrosion rate, hardness, and microstructure of alloys was examined. X-ray diffraction (XRD), open circuit potential, electrochemical tests (Tafel extrapolation method), and Macro hardness Brinell were used to study the effect of adding (B) in various amounts to alloys. Saliva was utilized as the corrosion solution for the testing. The inclusion of the alloy element (B) increased hardness and a decrease in particle size, as seen by the microstructures. Furthermore, the corrosion resistance of the master alloy improved next the addition, as shown by Corrosion potential has increased while corrosion current densities have decreased. The corrosion rate for A, A1, A2 and A3 was 14.50, 7.42, 2.03and 2.77 (mpy) respectively.