Open AccessSynthesis of Sodium Silicate from Rice Husk Ash as an Activator to Produce Epoxy-Geopolymer Cement
Author(s) -
Lia Handayani,
Sri Aprilia,
Abdullah Abdullah,
Cut Rahmawati,
A.M. Mustafa Al Bakri,
Ikmal Hakem Aziz,
Emy Aizat Azimi
Publication year - 2021
Publication title -
journal of physics. conference series
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.21
H-Index - 85
eISSN - 1742-6596
pISSN - 1742-6588
DOI - 10.1088/1742-6596/1845/1/012072
Subject(s) - geopolymer , sodium silicate , husk , materials science , cement , epoxy , fly ash , silicate , compressive strength , nuclear chemistry , composite material , chemistry , organic chemistry , botany , biology
Rice husk ash (RHA), a byproduct of the rice industry, is the primary source of amorphous silica for producing sodium silicate solutions to replace standard commercial sodium silicate in geopolymer mixture design. The effect of various concentrations of NaOH used as an activator to produce epoxy-geopolymer cement was studied. Three initial concentrations of NaOH were used (8, 10, and 12M) to examine the optimum dissolution and formation of silica oligomers that can function as the activator during the geopolymerization. The result indicated the increase of NaOH concentration raises the silica yield strength. The silica yield found was 65.84%, 70.53% and 72.06% on NaOH use of 8, 10, 12 M, respectively. IR-spectra results showed silica functional groups and the sodium silicate were successfully synthesized. The IR spectra indicated the appearance of hydroxyl bonds, which strengthen the geopolymer matrix. SEM results showed the C-S-H and N-A-S-H bonds in the geopolymer. With 10M NaOH, the compressive strength of the geopolymer cement paste was optimal at 27.53 MPa. Thus, Rice husk ash (RHA) is feasible to be used as an activator in high calcium fly ash-based epoxy geopolymer cement.