Open AccessStructure and functional properties of rapidly quenched TiNiCu alloys with high copper contents
Author(s) -
A. V. Shelyakov,
Nikolay Sitnikov,
Kirill Borodako,
I. A. Khabibullina,
A. A. Dyadechko
Publication year - 2021
Publication title -
journal of physics. conference series
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.21
H-Index - 85
eISSN - 1742-6596
pISSN - 1742-6588
DOI - 10.1088/1742-6596/1758/1/012036
Subject(s) - materials science , intermetallic , shape memory alloy , diffusionless transformation , martensite , alloy , amorphous solid , copper , hysteresis , metallurgy , phase (matter) , casting , composite material , microstructure , crystallography , condensed matter physics , chemistry , physics , organic chemistry
Thin materials exhibiting the shape memory effect, with a narrow temperature hysteresis, are required to create miniature and high-speed devices. Quasi-binary intermetallic TiNi-TiCu alloys with high copper contents (more than 10 at %) demonstrate the reversible martensitic transformation with a small (4-6 K) hysteresis. Alloys of the TiNi–TiCu system with a copper content of 30–40 at.% were fabricated in an amorphous state by the planar flow casting technique at a melt cooling rate of 10 6 K/s in the form of ribbons 30–50 μm thick. The alloy samples were subjected to dynamic crystallization using a single electric current pulse with duration of 5 ms. X-ray diffraction studies revealed almost fully martensitic state of the alloys with B19 structure at room temperature. TEM examination showed their structure to contain typical B19-martensite plates with a mean size of 20–80 nm. At the same time, the alloys exhibit a one-stage phase martensitic transformation B2↔B19 in the temperature range of (55÷75)°C, as well as pronounced shape memory effect, whose properties are largely determined by the structural parameters of the alloys.