Open AccessEffect of low nickel substitution on structure, morphology, and electrical transport of La0.7Sr0.2Ba0.1Mn1-xNixO3(x=0.02 and 0.05)
Author(s) -
Dicky Rezky Munazat,
Budhy Kurniawan,
Agung Imaddudin
Publication year - 2019
Publication title -
journal of physics. conference series
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.21
H-Index - 85
eISSN - 1742-6596
pISSN - 1742-6588
DOI - 10.1088/1742-6596/1402/6/066010
Subject(s) - electrical resistivity and conductivity , nickel , materials science , curie temperature , rietveld refinement , crystallography , crystal structure , condensed matter physics , analytical chemistry (journal) , chemistry , ferromagnetism , metallurgy , physics , electrical engineering , engineering , chromatography
The effect of low nickel substitution at Mn-site on structure, microstructure and electrical transport properties of La 0.7 Sr 0.2 Ba 0.1 Mn 1- x Ni x O 3 ( x = 0.02 and 0.05) were investigated. Samples were prepared by sol-gel method. From Rietveld refinement result, crystal structure of both samples were found to be Rhombohedral with R-3c (167) space group. Low nickel substitution at Mn-site shows that the Mn-O-Mn bond angle decreases and the Mn-O bond length increase which can link to Jahn-Teller distortion and double exchange. Scanning electron microscope (SEM) result reveals that nickel substitution leads to smaller grain size. Temperature-dependent resistivity ρ (T) has been measured at 15-285 K with zero field cooling. The experimental resistivity data were fitted by Percolation model. Percolation model can describe the electrical behavior of both samples based on electron-electron, electron-magnon, and electron-phonon scattering, and Kondo-like spin-dependent scattering at low temperature and adiabatic small polaron hopping at high temperature. It was found that nickel substitution decreases the metal-insulator transition temperature (T M-I ) from around 304 to 272 K, and Curie temperature (T c ) from around 330 to 310 K.