Fatigue strength of mash seam welded joints
Author(s) -
Tokaji,
Shiota,
Minagi,
Miyata
Publication year - 2000
Publication title -
fatigue and fracture of engineering materials and structures
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.887
H-Index - 84
eISSN - 1460-2695
pISSN - 8756-758X
DOI - 10.1046/j.1460-2695.2000.00240.x
Subject(s) - welding , materials science , fatigue limit , joint (building) , bending , composite material , fatigue testing , butt welding , butt joint , structural engineering , metallurgy , engineering
Reversed bending fatigue tests have been conducted using four series of mash seam welded joints obtained from the coupling of two different steels and plate thicknesses. Fatigue strength was evaluated and the effects of material property changes resulting from welding were studied. Fatigue strength of all series of the welded joints decreased slightly compared with that of the base steel. Type of steel and plate thickness in the welded samples exerted very little influence on fatigue strength. In the welded joints between steels with the same plate thickness, fatigue failure took place at a location away from the weld zone in the plate with the lower strength, while in the welded joints between plates of different thickness, failure occurred at the shoulder between the thin and thick plate, i.e. at the weld zone. Regardless of the type of steel and the plate thicknesses joined, fatigue strengths of the mash seam welded joints were slightly higher than those of the laser welded butt joints.