Fluoride release and uptake by four new fluoride releasing restorative materials
Author(s) -
Dionysopoulos P.,
Kotsanos N.,
Pataridou A.
Publication year - 2003
Publication title -
journal of oral rehabilitation
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.991
H-Index - 93
eISSN - 1365-2842
pISSN - 0305-182X
DOI - 10.1046/j.1365-2842.2003.00993.x
Subject(s) - fluoride , glass ionomer cement , dentistry , chemistry , nuclear chemistry , molar , medicine , inorganic chemistry
Summary The present study compared the initial fluoride release and release following refluoridation of a conventional glass–ionomer Ketac‐Molar (ESPE), a resin‐modified glass–ionomer, Vitremer (3M), and two compomers F‐2000 (3M) and Hytac (ESPE). Fifteen test specimens were prepared for each brand and immersed in deionized water. The fluoride released was measured every 2 days for 22 days. Refluoridation of the test specimens was done with solutions of 0·02, 0·04 and 0·2% NaF for 5 min on days 22, 30, 38 and 46. The fluoride released from recharged specimens was measured every 2 days until day 54. The fluoride release was highest during the first days after preparation, after which it decreased sharply and then more slowly. The four materials became ‘recharged’ with fluoride following repeated fluoride exposure in solution, the 0·2% solution being the most effective. From a clinical point of view, the results from this study imply that all the restorative materials tested may act as intra‐oral devices for the controlled slow release of fluoride at sites at risk of recurrent caries. Fluoride release and uptake by four new fluoride releasing restorative materials.