Open AccessHeterogeneous Metal-Free Hydrogenation over Defect-Laden Hexagonal Boron Nitride
Author(s) -
David J. Nash,
David Restrepo,
Natalia S. Parra,
Kyle E. Giesler,
Rachel A. Penabade,
Maral Aminpour,
Duy Le,
Zhanyong Li,
Omar K. Farha,
James K. Harper,
Talat S. Rahman,
Richard G. Blair
Publication year - 2016
Publication title -
acs omega
Language(s) - Uncategorized
Resource type - Journals
SCImago Journal Rank - 0.779
H-Index - 40
ISSN - 2470-1343
DOI - 10.1021/acsomega.6b00315
Subject(s) - catalysis , propene , cyclohexene , dehydrogenation , materials science , alkene , boron nitride , heterogeneous catalysis , boron , density functional theory , metal , hydrogen , chemical engineering , photochemistry , chemistry , inorganic chemistry , computational chemistry , organic chemistry , nanotechnology , metallurgy , engineering
Catalytic hydrogenation is an important process used for the production of everything from foods to fuels. Current heterogeneous implementations of this process utilize metals as the active species. Until recently, catalytic heterogeneous hydrogenation over a metal-free solid was unknown; implementation of such a system would eliminate the health, environmental, and economic concerns associated with metal-based catalysts. Here, we report good hydrogenation rates and yields for a metal-free heterogeneous hydrogenation catalyst as well as its unique hydrogenation mechanism. Catalytic hydrogenation of olefins was achieved over defect-laden h- BN ( dh -BN) in a reactor designed to maximize the defects in h- BN sheets. Good yields (>90%) and turnover frequencies (6 × 10 -5 -4 × 10 -3 ) were obtained for the hydrogenation of propene, cyclohexene, 1,1-diphenylethene, ( E )- and ( Z )-1,2-diphenylethene, octadecene, and benzylideneacetophenone. Temperature-programmed desorption of ethene over processed h -BN indicates the formation of a highly defective structure. Solid-state NMR (SSNMR) measurements of dh -BN with high and low propene surface coverages show four different binding modes. The introduction of defects into h- BN creates regions of electronic deficiency and excess. Density functional theory calculations show that both the alkene and hydrogen-bond order are reduced over four specific defects: boron substitution for nitrogen (B N ), vacancies (V B and V N ), and Stone-Wales defects. SSNMR and binding-energy calculations show that V N are most likely the catalytically active sites. This work shows that catalytic sites can be introduced into a material previously thought to be catalytically inactive through the production of defects.