Synthesis of Biogenic Silver Nanocatalyst and their Antibacterial and Organic Pollutants Reduction Ability

Plant-mediated nanoparticles are gaining popularity due to biologically active secondary metabolites that aid in green synthesis. This study describes a simple, environmentally friendly, dependable, and cost-effective production of silver nanoparticles utilizing Cucumis sativus and Aloe vera aqueous leaf extracts. The aqueous leaf extracts of Cucumis sativus and Aloe vera , which worked as a reducing and capping agent, were used to biosynthesize silver nanoparticles (AgNPs). The formation of surface plasmon resonance peaks at 403 and 405 nm corresponds to the formation of colloidal Ag nanoparticles. Similarly, the Bragg reflection peaks in X-ray diffraction patterns observed at 2θ values of 38.01°, 43.98°, 64.24°, and 77.12° representing the planes of [111], [200], [220], and [311] correspond to the face-centered cubic crystal structure of silver nanoparticles. Fourier transform infrared spectroscopy confirms that bioactive chemicals are responsible for the capping of biogenic silver nanoparticles. The size, structure, and morphology of AgNPs with diameters ranging from 8 to 15 nm were examined using transmission electron microscopy. Water contamination by azo dyes and nitrophenols is becoming a more significant threat every day. The catalytic breakdown of organic azo dye methyl orange (MO) and the conversion of para -nitrophenol (PNP) into para -aminophenol using sodium borohydride was evaluated using the prepared biogenic nanoparticles. Our nanoparticles showed excellent reduction ability against PNP and MO with rate constants of 1.51 × 10 -3 and 6.03 × 10 -4 s -1 , respectively. The antibacterial activity of the nanomaterials was also tested against four bacteria: Staphylococcus aureus , Klebsiella pneumoniae , Enterobacter , and Streptococcus pneumoniae . These biogenic AgNPs displayed effective catalytic and antibacterial characteristics by reducing MO and PNP and decreasing bacterial growth.