Synergetic Effect of Ti3+ and Oxygen Doping on Enhancing Photoelectrochemical and Photocatalytic Properties of TiO2/g-C3N4 Heterojunctions

To improve the utilization of visible light and reduce photogenerated electron/hole recombination, Ti 3+ self-doped TiO 2 /oxygen-doped graphitic carbon nitride (Ti 3+ -TiO 2 /O-g-C 3 N 4 ) heterojunctions were prepared via hydrothermal treatment of a mixture of g-C 3 N 4 and titanium oxohydride sol obtained from the reaction of TiH 2 with H 2 O 2 . In this way, exfoliated O-g-C 3 N 4 and Ti 3+ -TiO 2 nanoparticles were obtained. Simultaneously, strong bonding was formed between Ti 3+ -TiO 2 nanoparticles and exfoliated O-g-C 3 N 4 during the hydrothermal process. Charge transfer and recombination processes were characterized by transient photocurrent responses, electrochemical impedance test, and photoluminescence spectroscopy. The photocatalytic performances were investigated through rhodamine B degradation test under an irradiation source based on 30 W cold visible-light-emitting diode. The highest visible-light photoelectrochemical and photocatalytic activities were observed from the heterojunction with 1:2 mass ratio of Ti 3+ -TiO 2 o O-g-C 3 N 4 . The photodegradation reaction rate constant based on this heterojuction is 0.0356 min -1 , which is 3.87 and 4.56 times higher than those of pristine Ti 3+ -TiO 2 and pure g-C 3 N 4 , respectively. The remarkably high photoelectrochemical and photocatalytic performances of the heterojunctions are mainly attributed to the synergetic effect of efficient photogenerated electron-hole separation, decreased electron transfer resistance from interfacial chemical hydroxy residue bonds, and oxidizing groups originating from Ti 3+ -TiO 2 and O-g-C 3 N 4 .