Mechanical properties of talc‐ and (calcium carbonate)‐filled poly(vinyl chloride) hybrid composites
Author(s) -
Tuen Bee Soo,
Hassan Azman,
Abu Bakar Aznizam
Publication year - 2012
Publication title -
journal of vinyl and additive technology
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.295
H-Index - 35
eISSN - 1548-0585
pISSN - 1083-5601
DOI - 10.1002/vnl.20280
Subject(s) - talc , materials science , flexural strength , composite material , ultimate tensile strength , flexural modulus , calcium carbonate , izod impact strength test , composite number , filler (materials) , polyvinyl chloride , compression molding , vinyl chloride , polymer , mold , copolymer
The main objective of this study was to investigate and compare the mechanical properties of poly(vinyl chloride) (PVC) composites filled with calcium carbonate (CaCO 3 ), talc, and talc/CaCO 3 . Talc and CaCO 3 with different grades were incorporated into the PVC matrix. To produce the composites, the PVC resin, fillers, and other additives were first dry‐blended by using a laboratory mixer before being milled into sheets in a two‐roll mill. Test specimens were prepared by compression molding, after which the mechanical properties of the composites were determined. Single and hybrid filler loadings used were fixed at 30 phr (parts per hundred parts of resin). Talc‐filled composite showed the highest flexural modulus and the lowest impact strength, whereas uncoated, ground, 1‐μm CaCO 3 (SM 90) showed optimum properties in terms of impact strength and flexural modulus among all grades of CaCO 3 . It was selected to combine with talc at different ratios in the hybrid composites. The impact strength of the hybrid composites gradually increased with increasing SM 90 content, but the flexural and tensile properties showed an opposite behavior. Hybrid (10 phr talc):(20 phr SM 90)‐filled PVC composite reached a synergistic hybridization with balanced properties in impact strength, as well as flexural and tensile properties. J. VINYL ADDIT. TECHNOL., 2012. © 2012 Society of Plastics Engineers