Self‐compacting high performance fiber concrete for foundations: Part 2—Fiber orientation and distribution
Author(s) -
Grünewald Steffen,
Cotovanu Bogdan,
Rovers John,
Walraven Joost C.,
Taerwe Luc
Publication year - 2022
Publication title -
structural concrete
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.912
H-Index - 34
eISSN - 1751-7648
pISSN - 1464-4177
DOI - 10.1002/suco.202000441
Subject(s) - fiber , structural engineering , materials science , cracking , orientation (vector space) , cube (algebra) , shear (geology) , beam (structure) , composite material , engineering , mathematics , geometry
An investigation was executed into the applicability of self‐compacting high performance fiber concrete in foundations. The applied concrete has a concrete cube strength of about 110 MPa and contains 60 kg/m 3 hooked‐end steel fibers ( L F = 30 mm, D F = 0.38 mm). This publication consists of two parts: (1) Experimental assessment and verification of design rules and (2) assessment of fiber orientation and distribution. In the first part, experiments are described which were carried out to determine the pre‐ and post‐cracking strength properties, the shear resistance of short beams, the anchorage length of rebars, and the shear capacity of foundation slabs supported on piles. The test results were used for a verification and extension of design rules for fiber reinforced concrete (FRC) found in the fib Model Code 2010. The application of the FRC developed can lead to substantial savings in concrete and reinforcing steel. In the present second part, cross‐sections of two slabs and a beam of this testing series have been analyzed with regard to fiber orientation and distribution. An image analysis, executed on 111 concrete areas, indicates that a preferred fiber orientation could not be identified throughout the assessed elements. The data supports the conclusion of a good fiber distribution as well; a strong correlation was obtained for the data set of full images between measured and theoretical relation of fiber orientation and fiber density.