Study on Diversified Carbide Precipitation in High‐Strength Low‐Alloy Steel during Tempering
Author(s) -
Zhao Wei,
Zhou Hongwei,
Fang Liangwei,
Bai Fengmei,
Yi Hailong,
Ali Naqash,
Zhang Liqiang,
Zhen Guangwen
Publication year - 2021
Publication title -
steel research international
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.603
H-Index - 49
eISSN - 1869-344X
pISSN - 1611-3683
DOI - 10.1002/srin.202000723
Subject(s) - tempering , materials science , carbide , precipitation , nucleation , alloy , grain boundary , grain size , metallurgy , elongation , composite material , ultimate tensile strength , microstructure , chemistry , physics , organic chemistry , meteorology
Herein, the precipitation and mechanical properties of high‐strength low‐alloy steel (Q960E) under different tempering temperatures from 560 to 640 °C are investigated. Diversified precipitations (including MC, M 3 C, M 23 C 6 , and M 7 C 3 ) are formed during tempering. The size of the M 3 C, M 23 C 6 , and M 7 C 3 precipitates increases, as the temperature increases, and the precipitates are gradually spheroidized with an average size of less than 100 nm. MC‐type precipitates (where M = Nb and Ti) are produced at different tempering temperatures. When tempered at 600 °C, Q960E steel exhibits excellent mechanical properties, including a high strength and elongation with a good impact performance. At 600 °C, a large number of fine MC carbides with an average size of less than 25 nm are formed. MC and matrix exhibit the Baker–Nutting orientation relationship. Edge dislocations exist in the transition region between the MC nanophase and the matrix. These dislocations reduce the mismatch degree between the MC nanophase and the matrix and promote MC nucleation. Meanwhile, the steel retains many low‐angle grain boundaries when tempered at 600 °C, which is beneficial to its high strength.