Effect of Molybdenum and Cooling Regime on Microstructural Heterogeneity in Bainitic Steel Wires
Author(s) -
Ackermann Marc,
Resiak Bernard,
Buessler Pascal,
Michaut Bertrand,
Bleck Wolfgang
Publication year - 2020
Publication title -
steel research international
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.603
H-Index - 49
eISSN - 1869-344X
pISSN - 1611-3683
DOI - 10.1002/srin.201900663
Subject(s) - materials science , austenite , martensite , microstructure , metallurgy , molybdenum , ferrite (magnet) , thermomechanical processing , toughness , bainite , niobium , phase (matter) , continuous cooling transformation , composite material , chemistry , organic chemistry
Hot‐rolled wire is often further processed into complex components and therefore has to meet high demands on mechanical properties. Above all, during wire production, close control of the cooling parameters after hot rolling is required if strength and toughness must be set within narrow limits. Parameter studies are conducted in laboratory investigations to adjust bainitic microstructures, that consist of bainitic ferrite as the primary phase, whereas retained austenite films and martensite–austenite (M–A) constituents represent the secondary phase. Hot deformation trials with subsequent continuous cooling are conducted in a thermomechanical treatment simulator using two microalloyed steels with 0.25% C, 2% Mn, 0.03% Nb, and 0.03% Ti with or without Mo. The cooling parameters are set according to the process window of the cooling conveyor at the wire rod rolling mill. A microstructural analysis shows inhomogeneities in the appearance of the secondary phase depending on the cooling schedule. A quantitative analysis of the microstructural constituents indicates that the distribution function of the morphological characteristics of the M–A constituents corresponds to the mechanical properties. Therefore, cooling cycle and chemical composition are adjusted precisely to adjust the bainitic microstructure and achieve the desired mechanical properties.