Austenitizing Behavior of Laser Solid Formed Ultrahigh‐Strength 300 M Steel
Author(s) -
Liu Fenggang,
Lin Xin,
Song Menghua,
Song Kan,
Wang Feifan,
Li Qiuge,
Han Yifan,
Huang Weidong
Publication year - 2017
Publication title -
steel research international
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.603
H-Index - 49
eISSN - 1869-344X
pISSN - 1611-3683
DOI - 10.1002/srin.201600371
Subject(s) - austenite , materials science , ultimate tensile strength , metallurgy , martensite , atmospheric temperature range , microstructure , elongation , thermodynamics , physics
The influence of austenitizing treatment on the microstructure and mechanical properties of laser solid formed (LSFed) 300M steel is investigated within the austenitizing temperature range of 870–1050 °C. It is found that the dendritic segregation in 300M steel deposits (formed in the laser solid forming) gradually reduces with the increase of the austenitizing temperature, and even completely disappears when the austenitizing temperature reaches 1050 °C. Besides, the austenite grains and martensite packets in the LSFed 300M steel deposits changes little when the austenitizing temperature rises from 870 to 950 °C, but significantly coarsenes at the austenitizing temperature above 950 °C. The tensile test shows that the tensile strength of the samples reaches 2325 MPa after austenitizing heat treatment at 870 °C and, then, decreases slightly with the increase of the austenitizing temperature. For yields strength, it decreases slightly when the austenitizing temperature reaches 870–950 °C, while sharply decreases when the austenitizing temperature is above 950 °C. Moreover, a little effect of austenitizing temperature on the elongation and percentage reduction of area of the LSFed 300M steel is exhibited.