The Effect of Thermo‐Mechanical Processing Parameters on Microstructure and Mechanical Properties of a Low Carbon, High Strength Steel
Author(s) -
Li DaZhao,
Liu YongChang,
Cui TianXie,
Li JianMin,
Wang YuTian,
Fu PeiMao
Publication year - 2014
Publication title -
steel research international
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.603
H-Index - 49
eISSN - 1869-344X
pISSN - 1611-3683
DOI - 10.1002/srin.201300097
Subject(s) - materials science , lath , microstructure , elongation , austenite , toughness , metallurgy , bainite , composite material , plasticity , yield (engineering) , carbon fibers , martensite , ultimate tensile strength , composite number
High‐strength steel investigation is focused on the production of low carbon microalloying steel, particularly in the enhancement of steel strength through microstructure control, which is an urgent problem nowadays. This paper investigates the effect of various thermal mechanical control processing parameter on the properties and microstructures of Mn–Ti low carbon steels. The steel exhibited yield strength of 920 to 1069 MPa, elongation of approximately 10%, and impact absorbed energy between 16.7 and 45.3 J. At constant coiling temperature, more lath‐shaped carbonless ferrites, retained austenitic films with finer width, and island‐like twin martensites were generated. Strength and yield ratio increased with increase in finishing rolling temperature, but impact absorbed energy and total elongation decreased. When the finishing rolling temperature and coiling temperature were 860 and 220°C, respectively, the steel exhibited the highest strength and yield ratio but the lowest plasticity and toughness. At increased coiling temperature and unchanged finishing rolling temperature, more lath‐shaped ferrites with greater width were generated and gradually changed from carbonless to low‐bainite because of precipitations inside them. The width of the retained austenite increased with increase in coiling temperature. Thus, the strength and yield ratio decreased, but plasticity and impact toughness increased.