Phase Evolution and Mechanical Behavior of 0.36 wt% C High Strength TRIP‐Assisted Steel
Author(s) -
Ghosh Swarup Kumar,
Chattopadhyay Partha Protim
Publication year - 2012
Publication title -
steel research international
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.603
H-Index - 49
eISSN - 1869-344X
pISSN - 1611-3683
DOI - 10.1002/srin.201200090
Subject(s) - materials science , microstructure , austenite , trip steel , ultimate tensile strength , hardenability , metallurgy , isothermal process , ferrite (magnet) , continuous cooling transformation , annealing (glass) , elongation , work hardening , isothermal transformation diagram , composite material , bainite , thermodynamics , physics , alloy
Phase evolution in a 0.36 wt% C steel has been studied by thermodynamic calculation and dilatometric analysis with an aim to achieve high strength TRIP‐assisted steel with bainitic microstructure. The equilibrium phase fraction calculated as the function of temperature indicated the formation of δ‐ferrite (≈98%) at 1417°C. In contrast, similar calculation under para‐equilibrium condition exhibited transformation of δ‐ferrite to austenite at the temperature below 1300°C. During further cooling two‐phase (α+γ) microstructure has been found to be stable at the intercritical temperature range. The experimentally determined CCT diagram has revealed that adequate hardenability is achievable in the steel under continuous cooling condition at cooling rate >5°C s −1 . In view of the aforesaid results, the steel has been hot rolled and subjected to different process schedule conducive to the evolution of bainitic microstructure. The hot rolled steel has exhibited reasonably good tensile properties. However, cold deformation of the hot rolled sample followed by intercritical annealing and subsequent isothermal bainitic transformation has resulted in high strength (>1000 MPa) with attractive elongation due to the favorable work hardening condition during plastic deformation offered by the multiphase microstructure.