A Study of the Effect of Aluminium on the Mechanochemical Reduction of Hematite by Graphite
Author(s) -
Khaki Jalil Vahdati,
Panjehpour Masoud,
Kashiwaya Yoshiaki,
Ishii Kuniyoshi,
Bafghi Mohammad SheikhShab
Publication year - 2004
Publication title -
steel research international
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.603
H-Index - 49
eISSN - 1869-344X
pISSN - 1611-3683
DOI - 10.1002/srin.200405943
Subject(s) - aluminium , hematite , materials science , exothermic reaction , graphite , ball mill , metallurgy , endothermic process , melting point , composite material , chemistry , adsorption , organic chemistry
The effect of addition of small amounts of aluminium on mechano‐chemical reduction of hematite by graphite was studied. Various amounts of aluminium (0 to 10%) were added to a hematite‐graphite mixture, in which C/O ratio was 1:1. The hematite‐graphite‐aluminium mixtures were then subjected to ball milling followed by heating up reduction. The heating up reduction was carried out in Ar atmosphere, using TG‐DTA device. In TG‐DTA experiments, samples were heated by a constant heating rate of 10 °C/min from room temperature up to 1100 °C and maintained for 30 minutes at this temperature. To clarify the reactions which took place during milling and heating up reduction, the samples were subjected to XRD examinations. It was found that the heat generated during exothermic reaction of aluminothermic reduction of hematite promoted the endothermic reaction of carbothermic reduction. In the course of heating up reduction, the carbothermic reaction occurred just after aluminothermic reaction. Increasing of aluminum content from 0 to 10% in 2 hours ball milled samples decreased the temperature of carbothermic reaction from 1020 °C to about 860 °C. The further ball milling of the samples up to 5 and 10 hours, for the samples containing 10 and 5% aluminium respectively, caused the decrease of the temperature of aluminothermic and carbothermic reactions to around the melting point of aluminium.