Open AccessAchieving Low Lattice Thermal Conductivity in Half‐Heusler Compound LiCdSb via Zintl Chemistry
Author(s) -
Yang Xinxin,
Yuan Song,
Guo Kai,
Ni Heng,
Song Tao,
Lyu Wanyu,
Wang Da,
Li Han,
Pan Shusheng,
Zhang Jiye,
Zhao Jing-Tai
Publication year - 2022
Publication title -
small science
Language(s) - English
Resource type - Journals
ISSN - 2688-4046
DOI - 10.1002/smsc.202200065
Subject(s) - heusler compound , thermoelectric effect , thermal conductivity , thermoelectric materials , materials science , doping , figure of merit , condensed matter physics , lattice (music) , lattice vibration , metal , phonon , optoelectronics , thermodynamics , metallurgy , physics , acoustics , composite material
Half‐Heusler compounds usually possess ultrahigh power factors, while the large thermal conductivity hinders the further optimization of their thermoelectric properties. Herein, from the perspective of material design, a new half‐Heusler lattice with low lattice thermal conductivity by using Zintl chemistry based on the composition of LiCdSb is rationally constructed. The weak bonding within the polyanions combined with the resonance vibration modes of Li + contributes to the small lattice thermal conductivity of pristine LiCdSb as low as 3.2 W m −1 K −1 at 303 K and 0.85 W m −1 K −1 at 573 K. Ag doping is further conducted for boosting the electronic quality factor B E from 2.5 to 5.2 μW cm −1 K −2 due to the energy band modulation. As a result, a high power factor up to 21.35 μW cm −1 K −2 at 393 K is achieved in LiCd 0.94 Ag 0.06 Sb. In view of the low thermal conductivity, the figure of merit zT reaches 0.79 at 633 K. Herein, it is demonstrated that the half‐Heusler compound LiCdSb is a competitive thermoelectric parent, and low thermal conductivity can indeed be realized in half‐Heusler compounds through Zintl chemistry.