Mild‐Temperature Solution‐Assisted Encapsulation of Phosphorus into ZIF‐8 Derived Porous Carbon as Lithium‐Ion Battery Anode
Author(s) -
Yan Chengzhan,
Zhao Huaping,
Li Jun,
Jin Huile,
Liu Long,
Wu Wanyi,
Wang Jichang,
Lei Yong,
Wang Shun
Publication year - 2020
Publication title -
small
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 3.785
H-Index - 236
eISSN - 1613-6829
pISSN - 1613-6810
DOI - 10.1002/smll.201907141
Subject(s) - anode , materials science , chemical engineering , electrochemistry , porosity , composite number , inorganic chemistry , composite material , electrode , chemistry , engineering
The high theoretical capacity of red phosphorus (RP) makes it a promising anode material for lithium‐ion batteries. However, the large volume change of RP during charging/discharging imposes an adverse effect on the cyclability and the rate performance suffers from its low conductivity. Herein, a facile solution‐based strategy is exploited to incorporate phosphorus into the pores of zeolitic imidazole framework (ZIF‐8) derived carbon hosts under a mild temperature. With this method, the blocky RP is etched into the form of polyphosphides anions (PP, mainly P 5 − ) so that it can easily diffuse into the pores of porous carbon hosts. Especially, the indelible crystalline surface phosphorus can be effectively avoided, which usually generates in the conventional vapor‐condensation encapsulation method. Moreover, highly‐conductive ZIF‐8 derived carbon hosts with any pore smaller than 3 nm are efficient for loading PP and these pores can alleviate the volume change well. Finally, the composite of phosphorus encapsulated into ZIF‐8 derived porous carbon exhibits a significantly improved electrochemical performance as lithium‐ion battery anode with a high capacity of 786 mAh g −1 after 100 cycles at 0.1 A g −1 , a good stability within 700 cycles at 1 A g −1 , and an excellent rate performance.