Core–Shell Si/C Nanospheres Embedded in Bubble Sheet‐like Carbon Film with Enhanced Performance as Lithium Ion Battery Anodes
Author(s) -
Li Wenyue,
Tang Yongbing,
Kang Wenpei,
Zhang Zhenyu,
Yang Xia,
Zhu Yu,
Zhang Wenjun,
Lee ChunSing
Publication year - 2015
Publication title -
small
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 3.785
H-Index - 236
eISSN - 1613-6829
pISSN - 1613-6810
DOI - 10.1002/smll.201402072
Subject(s) - materials science , anode , lithium (medication) , carbon fibers , chemical engineering , silicon , battery (electricity) , composite number , carbonization , nanotechnology , composite material , electrode , optoelectronics , scanning electron microscope , medicine , power (physics) , chemistry , physics , quantum mechanics , engineering , endocrinology
Due to its high theoretical capacity and low lithium insertion voltage plateau, silicon has been considered one of the most promising anodes for high energy and high power density lithium ion batteries (LIBs). However, its rapid capacity degradation, mainly caused by huge volume changes during lithium insertion/extraction processes, remains a significant challenge to its practical application. Engineering Si anodes with abundant free spaces and stabilizing them by incorporating carbon materials has been found to be effective to address the above problems. Using sodium chloride (NaCl) as a template, bubble sheet‐like carbon film supported core–shell Si/C composites are prepared for the first time by a facile magnesium thermal reduction/glucose carbonization process. The capacity retention achieves up to 93.6% (about 1018 mAh g −1 ) after 200 cycles at 1 A g −1 . The good performance is attributed to synergistic effects of the conductive carbon film and the hollow structure of the core–shell nanospheres, which provide an ideal conductive matrix and buffer spaces for respectively electron transfer and Si expansion during lithiation process. This unique structure decreases the charge transfer resistance and suppresses the cracking/pulverization of Si, leading to the enhanced cycling performance of bubble sheet‐like composite.