Surface amine‐functionalization of UHMWPE fiber by bio‐inspired polydopamine and grafted hexamethylene diamine
Author(s) -
Hu Juncheng,
Feng Xia,
Liu Zhengyi,
Zhao Yiping,
Chen Li
Publication year - 2017
Publication title -
surface and interface analysis
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.52
H-Index - 90
eISSN - 1096-9918
pISSN - 0142-2421
DOI - 10.1002/sia.6203
Subject(s) - materials science , surface modification , composite material , fiber , epoxy , x ray photoelectron spectroscopy , adhesion , ultimate tensile strength , diamine , fourier transform infrared spectroscopy , polyethylene , scanning electron microscope , polymer chemistry , chemical engineering , engineering
Ultrahigh molecular weight polyethylene (UHMWPE) fibers exhibit excellent mechanical property, but their low surface activity limits the application in many fields. In this work, an efficient method was used to improve the surface activity and adhesion property of UHMWPE fibers. The amine functionalized UHMWPE fibers were prepared by the combination of bio‐inspired polydopamine (PDA) and grafted hexamethylene diamine (HMDA). The chemical structure of UHMWPE fibers was characterized by X‐ray photoelectron spectroscopy and attenuated total reflectance Fourier transform infrared spectroscopy. The surface morphologies and mechanical property of the fibers were investigated by scanning electron microscopy and tensile testing respectively. In addition, a single‐fiber pull‐out test was carried out to investigate the adhesion property of the fibers with epoxy resin matrix. The results showed that PDA was coated on the surface of UHMWPE fibers and then HMDA was successfully grafted on the PDA layers. The excellent mechanical property of UHMWPE fibers had no obvious change. Compared with the pristine UHMWPE fibers, the interfacial shear strength of the PDA coated UHMWPE fibers with the epoxy resin matrix improved by 28.3%, while the IFSS of the HMDA grafted UHMWPE fibers had an increase of 82.7%. Copyright © 2017 John Wiley & Sons, Ltd.