Evaluation of bias voltage effect on diamond‐like carbon coating properties deposited on tungsten carbide cobalt
Author(s) -
Zia Abdul Wasy,
Lee Seunghun,
Kim Jongkuk,
Kim Tae Gyu,
Song Jung II
Publication year - 2014
Publication title -
surface and interface analysis
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.52
H-Index - 90
eISSN - 1096-9918
pISSN - 0142-2421
DOI - 10.1002/sia.5400
Subject(s) - materials science , tungsten carbide , diamond like carbon , biasing , sputtering , raman spectroscopy , tungsten , coating , nanoindentation , composite material , sputter deposition , substrate (aquarium) , carbon fibers , metallurgy , thin film , nanotechnology , voltage , optics , oceanography , physics , quantum mechanics , geology , composite number
Diamond‐like carbon (DLC) coatings are getting new trends for cutting tool applications. In this research work, the DLC coatings were deposited on 15 × 15 × 5‐mm tungsten carbide cobalt substrates with variation of bias voltage from 0 to 500 V. The DLC films of 400 nm were deposited using filter cathode vacuum arc system, and 100‐nm chromium interlayer was deposited by sputtering. The optimized conditions for plasma pretreatment at different argon flow rates and deposition rates with bias variation were found. The effect of bias voltage on microstructure, tribology, adhesion, and mechanical properties were evaluated. The characterization techniques employed were field emission electron microscopy, Raman spectroscopy, wear test, SEM, scratch test, and nano‐indentation. The effect of substrate pretreatment on film adhesion was also evaluated. It was observed that etching rate increased with the increase in Ar flow rate while DLC deposition and sputtering rates decreased with increase in the bias voltage. The characterization suggests the DLC coatings deposited at 0 V bias as optimum condition because of showing the best results among all other conditions. Copyright © 2014 John Wiley & Sons, Ltd.