Increase in water resistance of paperboard by coating with poly(lactide)
Author(s) -
Rhim JongWhan,
Lee JunHo,
Hong SeokIn
Publication year - 2007
Publication title -
packaging technology and science
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.365
H-Index - 50
eISSN - 1099-1522
pISSN - 0894-3214
DOI - 10.1002/pts.767
Subject(s) - paperboard , coating , materials science , ultimate tensile strength , contact angle , composite material , elongation
Poly(lactide) (PLA)‐coated paperboards (PB) were prepared, and the effect of coating for improving water resistance of paperboard used for corrugated box liners was tested. Surface of paperboards became smoother through PLA coating, and their thickness and weight of coating increased depending on the concentration of the coating solution. Tensile strength of paperboard decreased, while elongation at break (E) increased after PLA coating. All water barrier properties tested, such as water vapour permeability (WVP), water absorptiveness (WA) and contact angle (CA) of water drop, indicated that water resistance of paperboard was improved through surface coating with PLA. WVP decreased from 4.8 to 25.5 times, and WA decreased from 11.9 to 17.9 times depending on the PLA concentration. The increase in water resistance of PLA‐coated paperboards was due to the hydrophobicity of PLA, which was proven through CA measurement. CA determined by both static and dynamic methods demonstrated the increase in initial CA of PLA‐coated paperboards, indicating an increased hydrophobicity of surface. All test results indicated that the optimum concentration of coating solution for improving water resistance of paperboard was 3 w/v % of PLA soulution. Copyright © 2007 John Wiley & Sons, Ltd.