Magnetotransport study on AlInN/(GaN)/AlN/GaN heterostructures
Author(s) -
Bayraklı Aydın,
Arslan Engin,
Fırat Tezer,
Özcan Şadan,
Kazar Özgür,
Çakmak Hüseyin,
Özbay Ekmel
Publication year - 2012
Publication title -
physica status solidi (a)
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.532
H-Index - 104
eISSN - 1862-6319
pISSN - 1862-6300
DOI - 10.1002/pssa.201127416
Subject(s) - heterojunction , materials science , condensed matter physics , van der pauw method , quantum well , magnetoresistance , electron mobility , shubnikov–de haas effect , electron , fermi gas , hall effect , optoelectronics , magnetic field , quantum oscillations , optics , physics , laser , quantum mechanics
We report the effect of a thin GaN (2 nm) interlayer on the magnetotransport properties of AlInN/AlN/GaN‐based heterostructures. Two samples were prepared (Sample A: AlInN/AlN/GaN and sample B: AlInN/GaN/AlN/GaN). Van der Pauw and Hall measurements were performed in the 1.9–300 K temperature range. While the Hall mobilities were similar at room temperature (RT), sample B had nearly twice as large Hall mobility as sample A at the lowest temperature; 679 and 889 cm 2 /Vs at RT and 1460 and 3082 cm 2 /Vs at 1.9 K for samples A and B. At 1.9–10 K, the longitudinal magnetoresistance was measured up to 9 T, in turn revealing Shubnikov–de Haas (SdH) oscillations. The carrier concentration, effective mass and quantum mobility of the two‐dimensional electron gas (2DEG) were determined from SdH oscillations. At 1.9 K, the 2DEG concentration of sample B was nearly seven times larger than of sample A (1.67 × 10 13 /cm 2 vs. 0.24 × 10 13 /cm 2 ). On the contrary, the quantum mobility was changed adversely nearly three times (sample B 2500 cm 2 /Vs and sample A 970 cm 2 /Vs). The increase of the 2DEG concentration was attributed to the existence of the GaN interlayer, which has strengthened the spontaneous polarization difference between the AlInN and GaN layers of the heterostructure. Hence, the stronger electric field at the 2DEG region bent the conduction band profile downwards and consequently the quantum mobility decreased due to the increased interface roughness scattering.