DC characterization of laser‐debonded GaN HEMTs
Author(s) -
Chan C. P.,
Leung K. K.,
Pilkuhn M.,
Surya C.,
Yue T. M.,
Pang G.,
Schweizer H.
Publication year - 2007
Publication title -
physica status solidi (a)
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.532
H-Index - 104
eISSN - 1862-6319
pISSN - 1862-6300
DOI - 10.1002/pssa.200622271
Subject(s) - materials science , characterization (materials science) , optoelectronics , laser , optics , nanotechnology , physics
We report experimental investigation of laser‐assisted debonding of GaN high electron mobility transistors (HEMTs) grown by metalorganic chemical vapor deposition (MOCVD) technique on sapphire substrates. The debonded HEMTs were transferred onto silicon substrate for better thermal dissipation during operation. Dc characterization indicated no degradation in the I–V characteristics as long as the optimized laser power was used in the debonding process. Transmission electron microscopy (TEM) of the AlGaN/GaN heterojunctions before and after the laser debonding process did not indicate any increase in the dislocation density at the heterointerface. We have also conducted detailed characterizations of the low‐frequency noise properties to investigate the defect properties over the entire active area of the device. Experimental data on the voltage noise power spectra measured from the same device before and after laser debonding indicated no significant change in the magnitude of the flicker noise over a wide temperature range. The results of XRD measurements revealed that the FWHM values before and after debonding are basically the same and also suggested that both out‐of‐plane tensile and in‐plane compressive stresses present were both removed after the laser processing. Our results clearly demonstrate that the laser‐assisted debonding process did not result in the increase in the material defect density. (© 2007 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)