Thermal Decomposition Enhancement of HMX by Bonding with TiO 2 Nanoparticles
Author(s) -
Zhu Qing,
Xiao Chun,
Xie Xiao,
Zheng Baohui,
Li Shangbin,
Luo Guan
Publication year - 2019
Publication title -
propellants, explosives, pyrotechnics
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.56
H-Index - 65
eISSN - 1521-4087
pISSN - 0721-3115
DOI - 10.1002/prep.201800277
Subject(s) - thermal decomposition , composite number , materials science , nanoparticle , decomposition , chemical engineering , nanomaterial based catalyst , composite material , nanotechnology , chemistry , organic chemistry , engineering
The appropriate structure and properties of a composite material, including the morphology, particle size, and bond strength, are very important for its performance and practical applications. The energetic material HMX (C 4 H 8 N 8 O 8 , cyclotetramethylenetetranitramine) is typically mixed with nanocatalysts to improve its thermal decomposition, which is advantageous for its detonation performance in practical applications. Inspired by the bioadhesion of mussels, a HMX@PDA@TiO 2 (HMX first coated with PDA film and second coated with TiO 2 nanoparticles) composite was developed in this study to greatly advance the thermal decomposition temperatures. A simple stirring process was used to prepare the composite from HMX and TiO 2 nanoparticles under dopamine solutions with different pH values. Nanocatalyst TiO 2 nanoparticles were anchored on the surface of HMX by reacting with the dopamine and polydopamine coatings. Compared with other reference samples, the thermal behavior of the obtained composite showed that the starting decomposition temperature was lower, at approximately 60 °C, and that the decomposition peak decreased by 35 °C, indicating that the composite properties should have great effects on the thermal performance of the materials. The findings offer a valuable composite preparation method to enhance the thermal behavior and the effect of the catalyst on the composite via bonding effects.