The chemistry and topography of stabilized and functionalized graphene oxide coatings
Author(s) -
Awaja Firas,
Tripathi Manoj,
Wong TszTing,
O'Brien Timothy,
Speranza Giorgio
Publication year - 2018
Publication title -
plasma processes and polymers
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.644
H-Index - 74
eISSN - 1612-8869
pISSN - 1612-8850
DOI - 10.1002/ppap.201800084
Subject(s) - x ray photoelectron spectroscopy , graphene , materials science , coating , oxide , chemical engineering , layer (electronics) , surface roughness , peek , carbon fibers , nanotechnology , surface finish , polymerization , composite material , polymer , composite number , metallurgy , engineering
Graphene oxide (GO) thin films and coatings are regarded as superior in quality to other materials especially for biomedical applications. However, the lack of stability and understanding of their structure and defects hinder their use in value added applications. Here, we describe our successful attempt at stabilizing, reducing and functionalizing GO through multiple plasma treatments with polymerizing (to deposit a crosslinking and compressing layer of diamond like carbon, DLC) and non‐polymerizing precursors (H 2 , O 2 , and N 2 ). The hybrid GO and DLC coatings on semi crystalline PEEK were evaluated using AFM, SEM, and XPS. The GO deposited layer showed roughness around 70 nm and, despite care, resulted in several wrinkles and particle aggregations. The hybrid coatings conformed to the roughness and crystalline features of PEEK. XPS showed that the DLC layer cross‐linked the GO nano‐flakes while not completely masking which enable the partial exposure of GO. The GO‐DLC hybrid interface is higher in thickness than the PEEK‐GO and is dominating the overall thickness of the hybrid structure ≈13 ± 1 μm. XPS measurements showed that the often unstable CO functional groups on the surface of the hybrid coating can be reduced by effective plasma treatment. Plasma treatments also generated CO functional groups that probably originated from the decomposed carboxyl groups. The plasma treatment also contributed to the reduction of GO. Treatment with H 2 was more effective in oxygen reduction than with the N 2 , however, treatment with N 2 increased the reactants on GO as N 2 is heavier tending to deposit more on a surface. Plasma treatment with O 2 increased the surface oxygen content further and hence more defects on the hybrid surface.