Novel cellulose nanofibers/barium titanate nanoparticles nanocomposites and their electrical properties
Author(s) -
Hassan Mohammad L.,
Ali Ashraf F.,
Salama Aliaa H.,
AbdelKarim Amal M.
Publication year - 2019
Publication title -
journal of physical organic chemistry
Language(s) - English
Resource type - Journals
SCImago Journal Rank - 0.325
H-Index - 66
eISSN - 1099-1395
pISSN - 0894-3230
DOI - 10.1002/poc.3897
Subject(s) - nanocomposite , barium titanate , thermogravimetric analysis , dielectric , nanoparticle , nanofiber , thermal stability , chemical engineering , materials science , scanning electron microscope , activation energy , dielectric loss , doping , cellulose , composite material , chemistry , nanotechnology , organic chemistry , optoelectronics , engineering
Green nanocomposite films from cellulose nanofibers/barium titanate (CNF/BT) with high homogeneity were successfully prepared by doping different ratio of BT nanoparticles (2.5 to 25 wt%) into CNF. Scanning electron microscope images showed homogenous distribution of BT in the CNF matrix. Thermogravimetric analysis results showed good thermal stability of the prepared nanocomposites. X‐ray diffraction analysis showed that the tetragonality of BT grains was retained in the composite samples. Addition of BT nanoparticles to CNF resulted in decreasing the tensile strength properties of the films. The dielectric properties were analyzed in detail with respect to frequency ranged from 0.1 Hz to 5 MHz, temperature ranged from 289 to 373 K, and BT loading. The high k values of the CNF/BT films were attributed to spontaneous polarization of BT particles. The dielectric constant of the nanocomposites increased by addition of BT nanoparticles up to 5 wt% and decreased afterwards. Hopping ionic conduction was proved as a conduction mechanism of the prepared nanocomposites. The activation energy of the conduction ranged from 0.4 to 0.08 eV. Moreover, the values of activation energy decreased as the doping level of BT nanoparticles increased.